Profiles for Repetier Host / Slic3r for A20M?

[BR365]

Hello,
I'm looking for profiles for the A20M to be used with Repetier Host and the Slic3r software.

The print of the test Dog is quite well but my own parts I tested were underextruded. So I increased extrudion to 120% and later to 150%, but it didn't help.

Or should I try a slower speed?

Is there a Config Bundle available for Slic3r?

Moritz

[Tomyuan]

Maybe mine's is not perfect.
But you can have a try:

Geeetech A20M.zip

(1.76 KiB) Downloaded 2518 times

[William]

Does the extruder working temperature achieve Preset temperature？

[BR365]

Does the extruder working temperature achieve Preset temperature？

Hello William,
I don't have a thermometer, therefore, I didn't check this. The Dog was printed with 205°C:



This looks very good, I think.

See Discussion here: http://www.geeetech.com/forum/viewtopic ... 08&t=68468

Thanks,
Moritz

[BR365]

Maybe mine's is not perfect.
But you can have a try:
Geeetech A20M.zip

This one is for ABS, isn't it?

Maybe interesting would be the E-Step value of Your setup. Maybe, my value isn't perfect. I didn't check yet.

Greetings
Moritz

[Tomyuan]

Hi,BR365


I am using the PETG for my A20M.
You can change the temp of the bed+temp of the hotend.
Then the others settings same as my PLA setting

[BR365]

Hi,BR365


I am using the PETG for my A20M.
You can change the temp of the bed+temp of the hotend.
Then the others settings same as my PLA setting

Thanks,
and could You tell me Your value for Esteps/mm?

Moritz

[Tomyuan]

If you want to calibrate your estep.
Refer to this vid：
https://www.youtube.com/watch?v=X3A9Ir2SreI

My estep is 457

[BR365]

If you want to calibrate your estep.
Refer to this vid：
https://www.youtube.com/watch?v=X3A9Ir2SreI

My estep is 457

Thanks, I will check.

My current value is 340, AFAIK.

[BR365]

Hi Vert,
I guess, the only possible solution is to remove these disks.
E-Steps changed to 422 (Calibration done), ...

No new result depending the stringing.

IMG_20190512_153329.jpg (188.35 KiB) Viewed 159102 times